Effective application of hyperbranched polyester resin in the coatings.
(1) hyperbranched polyester application in high-solids content coating.
Compact molecular structure, three-dimensional spherical structure, not easy to tangle between moleculars, compared with same molecular weight linear polymers, its solution has low viscosity at a higher solids content. (2) hyperbranched polyester application in the UV curable coating. Introducing hyperbranched polymer into the UV curing system, can overcome some of the disadvantages of linear oligomers, such as severe shrinkage of film, diluent volatilizing, toxicity, etc.
Thermosetting hyperbranched polyester with hydroxyl end groups, can control the crosslink density through the introduction of non-active/reactive end group. Light-curing coatings with acrylated polyesters, without adding photoinitiator, at a low intensity of UV irradiation, can cure film, and the film hardness, resistance to acetone, scratch resistance is good. (3) hyperbranched polyester application in powder coating.Powder coatings has disadvantages such as high curing temperature, large energy consumption, as well as not applied to heat-sensitive substrates.By introducing the hyperbranched polymer can overcome this disadvantage. Powder coatings generally cure time is 10 ~ 30 min, temperature is 170 ~ 200 ℃, which limit the powder coating application in the film substrate and heat sensitive substrates.The UV-curable powder coatings make up for this shortcoming, it can be used for heat-resistance substrate, low temperature curing, good fluidity, fast curing, etc. Weihai CY Dendrimer Technology Co. Ltd. -Professional Manufacturer for low cost dendritic polymers.

Polyamidoamine (PAMAM) dendrimer application in Coatings
Characteristics of dendritic PAMAM:
(1) Good hydrodynamics performance
(2) Unique viscosity behavior, has promising application prospects in coatings.
(3) Easy to forming-film, has promising application prospects in coatings.
(4) Having a large number of active surface group, so functionalized and modified end group is more convenient.
(5) A highly branched molecular structure determines its less prone to crystallization
(6) Having a good thermal stability

Application Example 1
Using half-generation dendrimer as a seed, styrene as the representative monomer to mix emulsion. The resulting average particle size of the polymer emulsion of ions between the 30-50nm, less than 100nm, and even distribution;
Example 2
Dendrimers with amino terminal group graft the silicon obtained epoxy curing agent, and uniformly dispersed in the epoxy resin, showed that the elastic modulus of cured material is lower than commonly used curing agent, and the heat resistance is improved.
Example 3
Using Dendrimers with amino terminal group as the epoxy resin curing agent, adding the theoretical amount and without diluent, at 20 ℃, usage time and gel time of such coatings are 6.0 and 2.4 times than ethylenediamine/epoxy System. And curing at 95 ℃, 120 ℃, 150 ℃, curing speed are 1.8 times, 3.4 times and 4.8 times than ethylenediamine/epoxy resin system.
Example 4
Dendrimers with amino terminal used as curing agent for the epoxy resin, at different temperatures and concentrations , the results shows that the gel time can be reduced under high temperature and reaction rate and kinetic constants are increased. The activation energy is significantly higher than the activation energy after the gel point.
Example 5
PAMAM Dendrimers have low melt viscosity, good compatibility and plentiful end group which can be modified, and it can be applied for coating system. Liang Hongbo etc. has reported on the polyamidoamine dendrimer modified end groups that by the introduction of crystallizable segments, can obtain semi-solid, semi-crystalline polymers which may be used as UV-curable powder coatings. This coating is solvent free, no VOC emissions, and has good raw material utilization, easy to operate. Weihai CY Dendrimer Technology Co. Ltd.-Professional Manufacturer for low cost dendritic polymers.

Films made from PAMAM are a novel and efficient cell anode catalyst for methanol fuel.
PAMAM-based film has good uniformity and the catalytic activity increases as the film generation enhanced. The catalytic ability of the film has been greatly improved compared to pure platinum catalysts, anti-drug capabilities have a greater enhancement, it’s a novel and efficient cell anode catalyst for methanol fuel. From "A direct catalyst for methanol fuel cell anode composite film and its preparation methods" Lin Shen, Luo Minghong, Zhang Xiaofeng, Fujian Normal University, Fuzhou, Fujian Normal University Technology Office Qishan campus, Application No. 200910112350.6. Weihai CY Dendrimer Technology Co. Ltd.-Professional Manufacturer for low cost dendritic polymers.